Functional Item
|
Test Method
|
test data
|
data unit
|
Basic performance
|
Glass filled
|
|
33
|
%
|
density
|
|
1.68
|
g/cm3
|
water absorption
|
|
0.9
|
%
|
Mold Shrinkage
|
|
0.1
|
%
|
Mechanical properties
|
Tensile strength
|
ASTM D638
|
175
|
MPa
|
elongation at break
|
ASTM D638
|
2.8
|
%
|
Flexural Strength
|
ASTM D790
|
222
|
MPa
|
Flexural Modulus
|
ASTM D790
|
11000
|
MPa
|
Lzodimpact strength
|
ASTM D256
|
100
|
J/m
|
Rockwell hardness
|
ASTM D785
|
125
|
R
|
Thermal Properties
|
Flammability
|
UL94
|
V-0
|
|
melting point
|
|
306
|
℃
|
glass transition temperature
|
|
125
|
℃
|
The main performance of PA9T
1. Nylon resin series, the minimum water imbibition
2. The size stability not caused by suction size change and mechanical strength decreased
3. The high heat resistance, spent 280 tin test won't produce bubbles, also suitable for high temperature lead-free soldering.
4. Poor liquidity, applicable in thin shape.
4. Low gas, gas is less than other nylon resin is not easy to pollution and corrosion of the mold, extend the mold use.
5. The crystallization speed, cooling time is short.
6. In the environment of high temperature, mechanical strength, rigid drop less, knit line strength, recycling is good. Injection molding process
Packaging materials used aluminum moisture proof bag, kaifeng can be performed immediately after processing.But, after opening the natural place particles will rise caused by moisture absorption water content, needs to be dry again.About dry condition again, if you use a hot air dryer, is about 120 ℃, 5 hours please as the reference standard.In addition, the drying temperature of 140 ℃ maximum recommended, recommended within 4 hours and drying time.
Molding conditions:
Melting point: 306 ℃
Recommend a nitrogen-treated barrel temperature: 310 ~ 330 ℃
Glass transition temperature: 125 ℃
Recommend the mold temperature 130-150 ℃
1, dry: between 130 ℃ / 3-4 hours
2, injection temperature: 290 ~ 310 ℃
3, mold temperature: 130 ~ 150 ℃
application
Mainly used for various electronic products, connectors, connectors, booth aspects such as products!Is suitable for the need to have the SMT electronic connector (especially suitable for lead-free soldering) is widely used in computers, digital cameras, mobile phones, etc.PA9T in personal computers, digital cameras, mobile phones and other electronic equipment into full play is the heat resistance, are widely used in memory connection and charging inserted into the mouth (connector).And in recent years due to environmental problems, in the welding of the electronic parts, use do not contain lead, the lead-free solder, has been widely popular, so Japan coke li GENESTAR high heat resistance are also more widespread high praise.PA9T besides heat resistance, sliding sex, even with drug resistance, actively promote the products in the field of auto parts and other broader applications.