Multiaxial warp knitted fabric, tape 3LF〔E567,0°‖E301,+45°‖E301,-45°〕is a non-crimp reinforcing material with 3-axial and layers structure knitted by polyester yarn, which is widely used in producing wind turbine blades, ship, sports, automobile, aerospace, tanks, pipelines, etc.
Multiaxial warp knitted fabric, tape 3LF〔E567,0°‖E301,+45°‖E301,-45°〕is a non-crimp reinforcing material with 3-axial and layers structure knitted by polyester yarn, which is widely used in producing wind turbine blades, ship, sports, automobile, aerospace, tanks, pipelines, etc. This material is a thick fabric, generally used in the rear part of a blade in the producing process, and the part of finished product is also available for processing and installing. The following introduction will be more detailed:
1 Descriptions of the name of the product
1.1 “3” indicates the amount of the layers,
1.2 “LF” means “Multi-layer fabric”,
1.3 The information in the square bracket describes the layer structure of the fabric, every layer connected by“//”. The correspondent letter “E” to each layer indicates the type of the glass in that layer will be E-glass. Meanwhile, the number of the layer indicates the elemental area and gravity, in unit g/m2, then followed by comma.
The structure type of each layer
——“0º”indicates that the array direction of the yarn parallels to the length direction of the fabric.
——“+45°”indicates that the array direction of the yarn and the across warp lie at an angle of about 45 degrees.
——“-45°”indicates that the array direction of the yarn and the across warp lie at an angle of about -45 degrees.
1.4 The letter “L” in the bracket indicates coil stitching
1.5 “1270”indicates the width of the multi-layer fabric, in the unit of mini meter.
1.6 “6” in the in the bracket indicates the cut will be 6 per inch.
2 Technical standards
Item
|
Inspection reference
|
Unit
|
Standard
|
Tensile strength
|
DIN EN ISO527-5
|
MPa
|
635
|
Tensile modulus of elasticity
|
DIN EN ISO527-5
|
Gpa
|
27.6
|
Rate of breaking elongation
|
DIN EN ISO527-5
|
%
|
2.61
|
Compressive strength
|
DIN EN ISO14126
|
MPa
|
432
|
Compressive modulus of elacticity
|
DIN EN ISO14126
|
Gpa
|
30.4
|
Breaking strain
|
DIN EN ISO14126
|
%
|
1.82
|
3 layer structure
Angle(°)
|
0
|
+45
|
-45
|
Raw material(tex)
|
E-glass fiber
|
E-glass fiber
|
E-glass fiber
|
Weight(g/m2)
|
567
|
301
|
301
|
4. Transportation
Should be transported by dry vehicles with canopy, and avoid mechanical damage, direct sunlight and moisture during the transportation.
5. Storage
Should be placed in dry and ventilated storage room, and avoid direct sunlight and heat. Stacking height should conform to GB / T 191 requirements.Temperature of 10 ℃ ~ 35 ℃, and relative humidity less than 85% will be the most appropriate conditions for storage. Storage period is generally 12 months.
6.for resin
The product is suitable for epoxy resi